Full metadata record
DC pole | Hodnota | Jazyk |
---|---|---|
dc.contributor.author | Čech, Jaroslav | |
dc.contributor.author | Haušild, Petr | |
dc.contributor.author | Siegl, Jan | |
dc.contributor.author | Junek, Lubomír | |
dc.contributor.author | Ernestová, Miroslava | |
dc.contributor.author | Bystrianský, Jaroslav | |
dc.contributor.editor | Polach, Pavel | |
dc.contributor.editor | Stuna, Lukáš | |
dc.date.accessioned | 2023-01-12T08:46:18Z | |
dc.date.available | 2023-01-12T08:46:18Z | |
dc.date.issued | 2019 | |
dc.identifier.citation | Zvyšování životnosti komponent energetických zařízení v elektrárnách. Sborník ze 14. konference: 24.– 26. září 2019. 1. vyd. Plzeň: Západočeská univerzita v Plzni, 2019, s. 89-92. | cs |
dc.identifier.isbn | 978-80-261-0885-6 | |
dc.identifier.uri | https://srni.vzuplzen.cz/wp-content/uploads/2021/04/sbornik2019.pdf | |
dc.identifier.uri | http://hdl.handle.net/11025/50879 | |
dc.description.abstract | V příspěvku je studován heterogenní svarový spoj potrubí z uhlíkové a austenitické ocele. Ve svařeném potrubí byly na rozhraní základní materiál – svarový kov nalezeny trhliny, které vznikly a šířily se mechanismem korozního praskání. Trhlina se šířila podél linie ztavení v oblasti promísení obou kovů. V této oblasti byly identifikovány změny v chemickém složení a zákalné struktury s výrazně vyšší tvrdostí oproti svařovaným kovům. | cs |
dc.description.sponsorship | TK01030108 (TA ČR) | cs |
dc.format | 4 s. | cs |
dc.format.mimetype | application/pdf | |
dc.language.iso | cs | cs |
dc.publisher | Západočeská univerzita v Plzni | cs |
dc.rights | © Západočeská univerzita v Plzni | cs |
dc.subject | heterogenní svarový spoj | cs |
dc.subject | kov | cs |
dc.subject | trhlina | cs |
dc.title | Charakterizace heterogenních svarových spojů | cs |
dc.title.alternative | Characterization of dissimilar metal welds | en |
dc.type | konferenční příspěvek | cs |
dc.type | conferenceObject | en |
dc.rights.access | openAccess | en |
dc.type.version | publishedVersion | en |
dc.description.abstract-translated | Heterogeneous dissimilar metal welds of carbon and austenitic stainless steel used in the piping systems were studied in this paper. The cracks were found in the welded pipeline at the interface between the base carbon steel and austenitic filler material. The stress corrosion cracking was identified as the cracking mechanism. The crack propagated along the fusion line in the mixing zone (area with higher diffusion) of both metals. In this area, changes in chemical composition and quenching structures with significantly higher hardness compared to the base metals were identified. | en |
dc.subject.translated | heterogeneous welded joint | en |
dc.subject.translated | metal | en |
dc.subject.translated | crack | en |
dc.type.status | Peer-reviewed | en |
Vyskytuje se v kolekcích: | Zvyšování životnosti komponent energetických zařízení v elektrárnách 2019 Zvyšování životnosti komponent energetických zařízení v elektrárnách 2019 |
Soubory připojené k záznamu:
Soubor | Popis | Velikost | Formát | |
---|---|---|---|---|
sbornik2019uvod_tiraz.pdf | Plný text | 3,69 MB | Adobe PDF | Zobrazit/otevřít |
sbornik2019-139-142.pdf | Plný text | 747,19 kB | Adobe PDF | Zobrazit/otevřít |
Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam:
http://hdl.handle.net/11025/50879
Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.